3mm PARA-Aramid Fiber Chopped Strands

Model NO.: XGPF1203
Width: 1.5D
Function: High Strength Fiber
Structure: Miscellaneous Chain Synthetic
Model: Xgpf1203
Colors: Yellowish
Fiber: PARA-Aramid
Density: 1.47g/cm3
P-Aramid Content: 100%
Average Fiber Length: 3mm
Tensile Strength: 19.4-21 Cn/Dtex
Tensile Modulus: 80gpa~120gpa
Elongation at Break: 2.5%-3.84%
Moisture: <0.2%
Trademark: XIANGU
Transport Package: 5kg Per Bag
Specification: ROHS
Origin: Guangdong
HS Code: 54021190
3mm para-aramid fiber chopped strands was chopped in 3mm by a special cutting equipment. This fiber has high strength and modulus, strong hydrogen bonding strength, strength up to 28 g/d or more, strength is 5-6 times of steel wire.specific modulus 2-3 times of it,toughness 2 times of it while weight is just 1/5 of the wire.Continuous using temperature range is extremely wide, long running in the range of -196 ºC to 204 ºC,no decomposition and melting at high temperature of 560 ºC,strength can maintain 75% through 100 hours at 200 ºC.also has good chemical solvent resistance, resisting acid and alkali, anti-aging, good adhesion to rubber. Usually it is used as a reinforcing material in the fields of thermoplastics, thermosetting plastics, high-temperature composite structures, brake pads, clutch linings, friction material, wear-resistant filler, cable sheathing, gaskets, slot insulation, phase insulation barrier, interturn insulation and so on.
 
SPECIFICATIONS:
Model: XGPF1203
Color: yellowish
Fiber type: Para-aramid
Density(g/cc) 1.47
Linear density of mono filament(D)  1.5
Filament diameter(μm) 12
Fiber length(mm) 3
Tensile strength( cN/dtex) 19.4-21
Elongation at break(%) 2.5-3.84
Tensile modulus(GPa) 80~120
Shrinkage(%) <0.2(190ºC×15m)
Moisture (%): <0.2

APPLICATION FIELDS:
1.Engineering Plastics,thermosetting resin,friction materials, automotive brakes,composite materials and Kevlar reinforced paper.
2.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.
3.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.
4.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.
 
STORAGE:
The 3mm para-aramid fiber chopped strands should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire

PACKAGING:
1.Inner black plastic film bags,net weight 5.00kg.gross weight 5.20kg.
2.Bag size:43*36*28cm,net weight 120.00kg.gross weight 150.00kg.

SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 20 pallets(each 180kg.two layers)be loaded into 20 feet container.total net weight is 2400kg.

Injection Sunglasses

Eyeglass Manufacturers ,Injection Sunglasses,Acetate Glasses

Able Trading Co., Limited , http://www.bogarsunglasses.com

Posted on